Hot Rolled XAR400/XAR500 Grade Wear Resistant steel
| Products | Hot Rolled XAR400/XAR500 Grade Wear Resistant Metal Steel Plate | ||||||
| Standard Grade | DIN: XAR300,XAR400, XAR450, XAR500, XAR600, DILLIDUR400V,DILLIDUR450V, DILLIDUR500V;X120Mn12; 1.3401; | ||||||
| SSAB:400,450,500,550,600; WELDOX700,WELDOX900,WELDOX960; | |||||||
| NF: FORA400,FORA500,Creusabro4800,Creusabro8000; | |||||||
| EN: QUARD400,QUARD450,QUARD500 ; RAEX320,RAEX400,RAEX450, RAEX500; DUrostat400,DUrostat450,DUrostat500; | |||||||
| JIS: JFE-EH360,JFE-EH400,JFE-EH500, WEL-HARD400, WEL-HARD500; SUMIHARD-K340,SUMIHARD-K400,SUMIHARD-K500 | |||||||
| GB: M360,NM400,NM450,NM500,NM550,NM600,NR360,NR400,B-HARD360, B-HARD400,B-HARD450,KN-55,KN-60,KN-63. | |||||||
| Thickness | 2-300mm (2-100mm usually used) | ||||||
| Width | 1000-3000mm (1000-2200mm usually used) | ||||||
| Length | 1000-12000mm or as your request | ||||||
| Surface | Clean, finishing,blasting and painting according to customer requirement | ||||||
| Process | Hot-rolled, Controlled rolling, Normalizing, Annealing, Tempering, Quenching, N+T, Q+T,and other delivery states are available as required | ||||||
| Certificate | API,ISO,SGS,BV,CE etc | ||||||
| Quality | MTC will be provided with goods, third part inspection is acceptable, for example BV,SGS. | ||||||
| Package | Standard export seaworthy package,suit for all kinds of transport,or as required. | ||||||
| Container Size | 20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High) | ||||||
| 40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High) | |||||||
| Trade term | Ex-Work,FOB,CNF,CFR,CIF,etc | ||||||
| Application | Widely used in a variety of architectural and engineering structures,such as | ||||||
| 1.) metal constructions such as buildings,bridges,ships; | |||||||
| 2.) transmission tower, reaction tower; | |||||||
| 3.) lifting transportation machinery; | |||||||
| 4.) industrial furnace;boilers | |||||||
| 5.) container frame, warehouse goods shelves, etc | |||||||
| Wear Resistant Steel Plate Chemical Composition and Mechanical Properties | |||||||||||||
| Chemical Composition(Max) | |||||||||||||
| Material | C | Si | Mn | P | S | Cr | Ni | Mo | Ti | Bt | Als | CEV | |
| NM300 | 0.23 | 0.7 | 1.6 | 0.025 | 0.015 | 0.7 | 0.5 | 0.4 | 0.05 | 0.0005-0.0006 | 0.01 | 0.45 | |
| NM360 | 0.25 | 0.7 | 1.6 | 0.025 | 0.015 | 0.8 | 0.5 | 0.5 | 0.05 | 0.0005-0.0006 | 0.01 | 0.48 | |
| NM400 | 0.3 | 0.7 | 1.6 | 0.025 | 0.01 | 1 | 0.7 | 0.5 | 0.05 | 0.0005-0.0006 | 0.01 | 0.55 | |
| NM450 | 0.35 | 0.7 | 1.7 | 0.025 | 0.01 | 1.1 | 0.8 | 0.55 | 0.05 | 0.0005-0.0006 | 0.01 | 0.6 | |
| NM500 | 0.38 | 0.7 | 1.7 | 0.02 | 0.01 | 1.2 | 1 | 0.65 | 0.05 | 0.0005-0.0006 | 0.01 | 0.65 | |
| NM550 | 0.38 | 0.7 | 1.7 | 0.02 | 0.01 | 1.2 | 1 | 0.7 | 0.05 | 0.0005-0.0006 | 0.01 | 0.72 | |
| NM600 | 0.38 | 0.7 | 1.9 | 0.02 | 0.01 | 1.5 | 1 | 0.7 | 0.05 | 0.0005-0.0006 | 0.01 | 0.76 | |
| Material | Tensile MPA | Elongation % | Impact energy -20ºC | HBW | |||||||||
| NM300 | ≥1000 | ≥14 | ≥24 | 270-300 | |||||||||
| NM360 | ≥1100 | ≥12 | ≥24 | 330-390 | |||||||||
| NM400 | ≥1200 | ≥10 | ≥24 | 370-430 | |||||||||
| NM450 | ≥1250 | ≥7 | ≥24 | 420-480 | |||||||||
| NM500 | ≥1250 | ≥7 | ≥24 | ≥470 | |||||||||
| NM550 | ≥1250 | ≥7 | ≥24 | ≥530 | |||||||||
| NM600 | ≥1250 | ≥7 | ≥24 | ≥570 | |||||||||